Company Details
Yangzhong Haiteng Fluorine Plastic Product Factory
Unit Price: | USD 3 - 3.5 / Piece/Pieces |
---|---|
Payment Type: | L/C,T/T,D/P |
Incoterm: | FOB,CFR,CIF |
Min. Order: | 100 Piece/Pieces |
Model No.: UHMWPE Part
Brand: HAITENG
Material: Composite Material
Color: White ,Black And Others
Mixed Material: PTFE
Packing: Customized Wooden Box
Application: Industry Application
Packaging: Paper Box
Productivity: 300000Pcs/Month
Transportation: Ocean,Land,Air
Place of Origin: Yangzhong China
Supply Ability: 300000Pcs/Month
Certificate: ISO
HS Code: 39209910
Port: Shanghai Port
Payment Type: L/C,T/T,D/P
Incoterm: FOB,CFR,CIF
Customized CNC Engineering Plastic UHMWPE Part
Characteristics
1. Very high-wear resistance, seven times wear resistance than steel, four times than PTFE
2. Very high anti-impact resistance, two times impact resistance than PC, five times than ABS.
3. Good self-lubrication, the same as PTFE, better than steel and brass appended lubricating oil.
4. Good anti-corrosion resistance, it has very stable chemicals property and can endure the corrosion of all kinds of corrosive medium and organic solvent in certain rang of temperature and humidity.
5. Very high-inadhesion resistance, the surface of product hardly affixes other material.
6. Very high-impact resistance, ten times impact resistance than PA66, eight times than PTFE.
7. Good low temperature resistance, in liquefied nitrogen (- 196ºC), it still has the prolongation.
few other materials can reach to this performance.
8. Non-toxic and clean property, UHMW-PE material that made by Guangzhou Engineering Plastics Industries (Group) Company.
Images
PROPERTIES | Unit | Value |
I.Physical Properties | ||
Density | g/cm3 | 0.96 |
Water absorption 24hrs | % | 0.01 |
II.Thermal Properties | ||
Heat deflection temperature - HDT/A | ºC | 42 |
Min. service temperature | ºC | -269 |
Max. service temperature-Long Term | ºC | 90 |
Thermal conductivity at 23 ºC | W/(K*m) | 0.42 |
Coefficient of linear thermal expansion | 10-4*K-1 | 2 |
Flammability Rating(6mm thickness) | - | HB |
III.Mechanical Properties at 23ºC | ||
Tensile strength at yield | MPa | 17 |
Tensile strength at break | Mpa | 40 |
Elongation at break | % | >50 |
Modulus of elasticity after tensile test | MPa | 650 |
Modulus of elasticity after flexural test | MPa | 800 |
Hardness - Shore D | | 61 |
Charpy impact strength | kJ/m2 | N. B. |
Friction coefficient | | 0.25 |
IV.Electrical Properties at 23ºC | ||
Dielectric constant at 1 MHz | 106Hz | 3.1 |
Dielectric loss factor at 1 MHz | 106Hz | 0.0001 |
Volume resistively | Ohm (Ω) * cm | >1014 |
Surface resisively | Ohm (Ω) | >1011 |
Dielectric strength | kV/mm | 45 |
NOTE: 1 g/cm3 = 1,000 kg/m3, 1 Mpa = 1 N/mm2, 1kV/mm = 1 MV/m | ||
| | |