UHMW-PE Plastic Parts with Wear Resistance

Share to:

Unit Price:

USD 2.3 - 2.5 / Piece/Pieces

Payment Type:

L/C,T/T,D/P

Incoterm:

FOB,CFR,CIF

Min. Order:

100 Piece/Pieces

Basic Info

Model No.: UHMWPE Part

Brand: HAITENG

Material: Composite Material

Color: White ,Black And Others

Mixed Material: PTFE

Packing: Customized Wooden Box

Application: Industry Application

Additional Info

Packaging: Paper Box

Productivity: 300000Pcs/Month

Transportation: Ocean,Land,Air

Place of Origin: Yangzhong China

Supply Ability: 300000Pcs/Month

Certificate: ISO

HS Code: 39209910

Port: Shanghai Port

Payment Type: L/C,T/T,D/P

Incoterm: FOB,CFR,CIF

Product Description

UHMW-PE Plastic Parts with Wear Resistance

UHMW-PE(Ultra high Molecular Weight Polyethylene)is a thermoplastic engineering plastic

with the average molecular weight more than 9.2 million (100% Virgin UHMW-PE Raw Material).

This kind of material with five top performance of high-wear-resistance, good-chemical resistance, low-temperature resistance, self-lubrication and high-impact resistance, which is regarded as a "surprised" engineering plastic of excellent comprehensive capacity and competitive price. Yangzhong Haiteng Fluorine Plastic Factory has studied and applied this material in many

industries for many years.

Images

Customized Uhmwpe Part

Characteristics
-Excellent wear resistance
-Can work under the temperature -200°C to +80°C
-Impact and noise reduction
-Chemical resistant
-No water absorption
-Anti-adhesive
-Food safe
-Light weight

Technical Data Sheet

PROPERTIES	Unit	Value
I.Physical Properties
Density	g/cm3	0.96
Water absorption 24hrs	%	0.01
II.Thermal Properties
Heat deflection temperature - HDT/A	ºC	42
Min. service temperature	ºC	-269
Max. service temperature-Long Term	ºC	90
Thermal conductivity at 23 ºC	W/(K*m)	0.42
Coefficient of linear thermal expansion	10-4*K-1	2
Flammability Rating(6mm thickness)	-	HB
III.Mechanical Properties at 23ºC
Tensile strength at yield	MPa	17
Tensile strength at break	Mpa	40
Elongation at break	%	>50
Modulus of elasticity after tensile test	MPa	650
Modulus of elasticity after flexural test	MPa	800
Hardness - Shore D		61
Charpy impact strength	kJ/m2	N. B.
Friction coefficient		0.25
IV.Electrical Properties at 23ºC
Dielectric constant at 1 MHz	106Hz	3.1
Dielectric loss factor at 1 MHz	106Hz	0.0001
Volume resistively	Ohm (Ω) * cm	>1014
Surface resisively	Ohm (Ω)	>1011
Dielectric strength	kV/mm	45
NOTE: 1 g/cm3 = 1,000 kg/m3, 1 Mpa = 1 N/mm2, 1kV/mm = 1 MV/m