HAITENG Customized Delrin/POM Machine Parts China Manufacturer

Home > Products > POM Products > Other POM Products > HAITENG Customized Delrin/POM Machine Parts

HAITENG Customized Delrin/POM Machine Parts

Share to:

Unit Price:

USD 1.5 - 2 / Piece/Pieces

Payment Type:

L/C,T/T,D/P

Incoterm:

FOB,CFR,CIF

Min. Order:

200 Piece/Pieces

Basic Info

Model No.: POM Machine Part

Brand: HAITENG

Material: Composite Material

Color: White ,Black And Others

Packing: Customized Wooden Box

Application: Industry Application

Mixed Material: POM

Density: 1.5g/cm3

Customized: As Per Drawings Or Samples

Processing Tech: Turning,Milling,Drilling,Sawing,etc

Additional Info

Packaging: Paper Box

Productivity: 300000Pcs/Month

Transportation: Ocean,Land,Air

Place of Origin: Yangzhong China

Supply Ability: 300000Pcs/Month

Certificate: ISO

HS Code: 39209910

Port: Shanghai Port

Payment Type: L/C,T/T,D/P

Incoterm: FOB,CFR,CIF

Product Description

HAITENG Customized Delrin/POM Machine Parts by CNC Lathe Machine

Characteristics
-High surface hardness
-Good wear resistance
-Excellent machinability
-Nice self-lubricating properties
-Good dimensional stability
-Low water absorption
-Oil resistant
-Work under the temperature of -40-100ºC

The common document files accepted are : *.pdf/*.dwg/*.IGS/*.step/*.prt/*.sldprt Just send the drawings to us, we will handle the rest for you.

Images

POM Machine Parts

Contact Info

POM parts by CNC Machine

Technical data sheet

PROPERTIES	Unit	Value
I.Physical Properties
Density	g/cm3	1.45
Water absorption 24hrs	%	< 0.3
II.Thermal Properties
Heat deflection temperature - HDT/A	ºC	110
Min. service temperature	ºC	-40
Max. service temperature	ºC	100
Thermal conductivity at 23 ºC	W/(K*m)	0.31
Coefficient of linear thermal expansion	10-4*K-1	1.2
Flammability Rating(6mm thickness)	-	HB
III.Mechanical Properties at 23ºC
Tensile strength at yield	MPa	63
Tensile strength at break	Mpa	-
Elongation at break	%	31
Modulus of elasticity after tensile test	MPa	2,700
Modulus of elasticity after flexural test	MPa	-
Hardness - Shore D		83
Charpy impact strength	kJ/m2	N. B.
Friction coefficient		0.35
IV.Electrical Properties at 23ºC
Dielectric constant at 1 MHz	106Hz	3.8
Dielectric loss factor at 1 MHz	106Hz	0.005
Volume resistively	Ohm (Ω) * cm	>1013
Surface resisively	Ohm (Ω)	>1013
Dielectric strength	kV/mm	40

The machining process include below
1.Turning: For parts which have high surface requirement, wide-head cutters are better. When processing thin walled and soft material, cutters like knife are recommended.
2. Milling: When milling the surface, end-milling is more cost-effective than circular milling. For circular and forming cutter, it should have less than two cutter edges. In this case, the tolerance caused due to the edge vibration can be lowered to the minimum.
3. Sawing: Thin saws are usually used to saw thick parts to avoid the heating caused by friction. It would be better to use sharp and big sawblade.
4. Drilling: When drilling the solid materials, make sure to use sharp drill, otherwise the increasing pressure during drilling will cause material cracks.
The common document files accepted are : *.pdf/*.dwg/*.IGS/*.step/*.prt/*.sldprt Just send the drawings to us, we will handle the rest for you.